Mauritzon, Inc.
TTS-10HUV consists of two sheets of high-strength polyethylene film laminated together with a third layer of molten polyethylene. A heavy-duty scrim reinforcement placed between these plies greatly enhances tear-resistance and increases service life. Heavy-duty diamond reinforcement responds to tears immediately by surrounding and stopping the tear. Please Note: tarpaulins may actually finish 3-5% less in size for cut-sized. For finished sizes, please request with order.
Unit of Measure

Specifications

Size

N/A 6 x 8 ft10 x 12 ft10 X 20 ft12 X 15 ft12 X 20 ft12 X 24 ft16 X 20 ft20 X 20 ft20 X 30 ft24 X 24 ft24 X 30 ft30 X 30 ft40 X 40 ft50 X 50 ft100 X 100 ft

Thickness

N/A 12 mil

Weight

N/A 7 oz/yd²

Material Test Results

Mullen Burst1 N/A 175 psi1207 kPa

Appearance

N/A Clear

Nominal Thickness

N/A 10 mil0.25 mm

Weight per MSF

N/A 51 lb23 kg

Construction

N/A Extrusion laminated scrim reinforced
"1" Tensile Strength2 N/A 57 lb254 N
Elongation at Break3 N/A 800 %
Grab Tensile Strength4
N/A 90 lb400 N
Trapezoid Tear5
N/A 69 lb307 N
Hydrostatic Resistance6 N/A 90 psi621 kPa

Minimum Use Temperature

N/A -57 ºC-70 ºF

Maximum Use Temperature

N/A 82 ºC180 ºF
Permeability WVTR (g/100in/2day)7 N/A 0.0185
Permeability WVTR (g/m2/day)8 N/A 0.2868
U.S. Perms Rating9 N/A 0.0418
Metric Perms Rating10 N/A 0.0275
  • 1 ASTM D751
  • 2 ASTM D751
  • 3 ASTM D751
  • 4 ASTM D751
  • 5 ASTM D4533
  • 6 ASTM D751
  • 7 ASTM E96
  • 8 ASTM E96
  • 9 ASTM E96
  • 10 ASTM E96